Tha inbhean àrainneachd an EU RoHS 2.0 ag iarraidh gum bi susbaint luaidhe (Pb) nas ìsle na 1000ppm. .Tha coileanadh gearraidh an C17200 seo math cuideachd.
1. Dèanamh ceimigeach de luaidhe ìosal C17300
| Modail | Be | Ni+Co | Ni+Co+Fe | Pb | Cu |
| C17300 | 1.8-2.0 | ≥0.20 | ≤0.6 | ＜0.1 | Fuigheall |
2. Feartan corporra agus meacanaigeach deluaidhe ìosalC17300
| Stàite | Làimhseachadh teas ( ℃） | Trast-thomhas (mm) | Neart tensile (MPa) | Neart toraidh (MPa) | Leudachadh 4xD(%) | cruas | Giùlan dealain (IACS,%) | |
| HV0.5 | HRB no HRC | |||||||
| TB00 | 775 ℃ ~ 800 ℃ | Uile | 410-590 | mu 140 | mu 20 | 159-162 | B45-B85 | 15-19 |
| TD04 | 775 ℃ ~ 800 ℃ Fuasgladh + Pròiseas Fuar Cruadhachadh | 8-20 | 620-860 | mu 520 | ＞ 8 | 175-257 | B88-B102 | 15-19 |
| 0.6-8 | 620-900 | mu 520 | ＞ 8 | 175-260 | B88-B103 | |||
| TH04 | 315 ℃ x1 ~ 2 uair a thìde | 8-20 | 1140-1380 | mu 930 | mu 20 | 345-406 | C27-C44 | 23-28 |
| 0.6-8 | 1210-1450 | mu 1000 | ＞ 4 | 354-415 | C38-C45 | |||